(10) VISUAL INSPECTION AND OTHER NDE METHODS AND SYMBOLS Flashcards

1
Q

Q10-1

Which of the following nondestructive testing methods are limited to the detection of surface discontinuities?

a. visual
b. penetrant
c. radiographic
d. a and b above
e. b and c above

A

Q10-1

Which of the following nondestructive testing methods are limited to the detection of surface discontinuities?

D. a and b above

a. visual
b. penetrant

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
2
Q

Q10-2

To be most effective, visual inspection should be performed:

a. before welding
b. during welding
c. after welding
d. all of the above
e. none of the above

A

Q10-2

To be most effective, visual inspection should be performed:

D. all of the above

a. before welding
b. during welding
c. after welding

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
3
Q

Q10-3

The time period during which the penetrant remains on the surface of the part allowing it to be drawn into any surface discontinuities is called:

a. waiting time
b. penetrating time
c. soak time
d. dwell time
e. none of the above

A

Q10-3

The time period during which the penetrant remains on the surface of the part allowing it to be drawn into any surface discontinuities is called:

d. dwell time

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
4
Q

Q10-4

Which type of magnetizing current provides the best iron particle mobility?

a. AC
b. DC
c. DCEP
d. b and c above
e. all of the above

A

Q10-4

Which type of magnetizing current provides the best iron particle mobility?

a. AC

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
5
Q

Q10-5

What MT technique could be used for the discovery of longitudinal flaws?

a. head shot (circular magnetism)
b. side shot
c. coil shot (longitudinal magnetization)
d. a and b above
e. b and c above

A

Q10-5

What MT technique could be used for the discovery of longitudinal flaws?

a. head shot (circular magnetism)

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
6
Q

Q10-6

Which of the following magnetizing methods produce a circular magnetic field in the test piece?

a. head shot
b. passing an electrical current through the part
c. prod
d. all of the above
e. none of the above

A

Q10-6

Which of the following magnetizing methods produce a circular magnetic field in the test piece?

D. all of the above

a. head shot
b. passing an electrical current through the part
c. prod

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
7
Q

Q10-7

Which of the following magnetizing methods can produce a longitudinal magnetic field in the test piece?

a. head shot
b. coil shot
c. yoke
d. a and b above
e. b and c above

A

Q10-7

Which of the following magnetizing methods can produce a longitudinal magnetic field in the test piece?

E. b and c above

b. coil shot
c. yoke

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
8
Q

Q10-8

What NDT method is best for evaluating subsurface porosity?

a. PT
b. MT
c. RT
d. VT
e. all of the above

A

Q10-8

What NDT method is best for evaluating subsurface porosity?

c. RT

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
9
Q

Q10-9

Which of the following statements is correct for radiographic testing?

a. A reduction in thickness will produce a lighter image on the film.
b. A low density discontinuity will produce a lighter image on the film.
c. A high density discontinuity will produce a lighter image on the film.
d. a and b above
e. b and c above

A

Q10-9

Which of the following statements is correct for radiographic testing?

c. A high density discontinuity will produce a lighter image on the film.

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
10
Q

Q10-10

Radiographic testing (RT) can be performed using which of the following?

a. X-ray machine
b. Cesium 137
c. Iridium 192
d. Cobalt 60
e. all of the above

A

Q10-10

Radiographic testing (RT) can be performed using which of the following?

E. all of the above

a. X-ray machine
b. Cesium 137
c. Iridium 192
d. Cobalt 60

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
11
Q

Q10-11

MT can be used most effectively to inspect which of the following?

a. austenitic stainless steel welds on carbon steel
b. austenitic stainless steel welds on stainless steel
c. carbon steel welds on carbon steel
d. a and b above
e. b and c above

A

Q10-11

MT can be used most effectively to inspect which of the following?

c. carbon steel welds on carbon steel

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
12
Q

Q10-12

Which of the following discontinuities will not usually be revealed using RT?

a. crack
b. incomplete joint penetration
c. porosity
d. lamination
e. none of the above

A

Q10-12

Which of the following discontinuities will not usually be revealed using RT?

d. lamination

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
13
Q

Q10-13

What device is used during radiography to indicate the resolution sensitivity of a radiograph?

a. IQI
b. dosimeter
c. lead screen
d. all of the above
e. none of the above

A

Q10-13

What device is used during radiography to indicate the resolution sensitivity of a radiograph?

a. IQI

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
14
Q

Q10-14

Which nondestructive test method uses sound energy as a probing medium?

a. MT
b. RT
c. UT
d. PT
e. ET

A

Q10-14

Which nondestructive test method uses sound energy as a probing medium?

c. UT

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
15
Q

Q10-15

The process whereby ultrasonic indications are related to dimensions in a test standard is referred to as:

a. setup
b. calibration
c. standardization
d. synchronization
e. none of the above

A

Q10-15

The process whereby ultrasonic indications are related to dimensions in a test standard is referred to as:

b. calibration

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
16
Q

Q10-16

As-welded groove welds are usually inspected ultrasonically using what technique?

a. straight beam
b. shear wave
c. angle beam
d. b and c above
e. all of the above

A

Q10-16

As-welded groove welds are usually inspected ultrasonically using what technique?

D. b and c above

b. shear wave
c. angle beam

17
Q

Q10-17

Capillary action plays a role in which NDT method?

a. ET
b. UT
c. RT
d. PT
e. MT

A

Q10-17

Capillary action plays a role in which NDT method?

d. PT

18
Q

Q10-18

Which NDT method is considered to be a true volumetric test?

a. RT
b. UT
c. PT
d. MT
e. VT

A

Q10-18

Which NDT method is considered to be a true volumetric test?

b. UT

19
Q

Q10-19

Which NDT method uses an alternating current coil?

a. MT
b. UT
c. ET
d. a and c above
e. b and c above

A

Q10-19

Which NDT method uses an alternating current coil?

D. a and c above

a. MT
c. ET

20
Q

Q10-20

Changes in heat treatment can be measured using which NDT method?

a. ET
b. RT
c. MT
d. UT
e. none of the above

A

Q10-20

Changes in heat treatment can be measured using which NDT method?

a. ET

21
Q

Q10-21

Which of the following NDT methods can detect surface cracks?

a. RT
b. VT
c. ET
d. PT
e. all of the above

A

Q10-21

Which of the following NDT methods can detect surface cracks?

E. all of the above

a. RT
b. VT
c. ET
d. PT

22
Q

Q10-22

Which NDT method is most likely to reveal subsurface laminations in a rolled plate?

a. RT
b. UT
c. ET
d. MT
e. none of the above

A

Q10-22

Which NDT method is most likely to reveal subsurface laminations in a rolled plate?

b. UT

23
Q

Q10-23

Piezoelectricity is a property used by which NDE method?

a. ET
b. UT
c. RT
d. a and b above
e. b and c above

A

Q10-23

Piezoelectricity is a property used by which NDE method?

b. UT

24
Q

Q10-24

Which is the best technique for orienting magnetic lines of force when conducting MT testing?

a. two directions
b. single direction
c. residual magnetism
d. all of the above
e. none of the above

A

Q10-24

Which is the best technique for orienting magnetic lines of force when conducting MT testing?

a. two directions

25
Q

Q10-25

What resolution sensitivity is normally required for RT?

a. 2%
b. 4%
c. 5%
d. 7%
e. 9%

A

Q10-25

What resolution sensitivity is normally required for RT?

a. 2%

26
Q

Q10-26

What is the basic element of evaluation in any quality control program?

a. radiographic testing
b. penetrant testing
c. visual inspection
d. all of the above
e. none of the above

A

Q10-26

What is the basic element of evaluation in any quality control program?

c. visual inspection

27
Q

Q10-27

When should the applicable job documents be reviewed?

a. after the job is completed
b. before welding begins
c. at any time when information is necessary
d. a and b above
e. b and c above

A

Q10-27

When should the applicable job documents be reviewed?

E. b and c above

b. before welding begins
c. at any time when information is necessary

28
Q

Q10-28

What is the role of the AWS CWI in NDE?

a. see that inspections are done
b. verify personnel qualifications for NDE inspection
c. prepare proper records
d. see that proper records are maintained
e. all of the above

A

Q10-28

What is the role of the AWS CWI in NDE?

E. all of the above

a. see that inspections are done
b. verify personnel qualifications for NDE inspection
c. prepare proper records
d. see that proper records are maintained

29
Q

Q10-29

A number in parentheses just above or below a test symbol describes:

a. the length of weld to be tested
b. the extent of testing
c. the number of tests to perform
d. the type of test to perform
e. none of the above

A

Q10-29

A number in parentheses just above or below a test symbol describes:

c. the number of tests to perform

30
Q

Q10-30

A number to the right of a nondestructive testing symbol refers to the:

a. number of tests to perform
b. the length of weld to be tested
c. the applicable quality standard
d. the test procedure to use
e. none of the above

A

Q10-30

A number to the right of a nondestructive testing symbol refers to the:

b. the length of weld to be tested

31
Q

Q10-31

Test information above the reference line refers to the arrow side.

a. true
b. false

A

Q10-31

Test information above the reference line refers to the arrow side.

b. false

32
Q

2008 ANSWER KEY—CHAPTER 10

A

Q10-1 d (pg. 10-15)
Q10-2 d (pg. 10-3)
Q10-3 d (pg. 10-13, 10-15)
Q10-4 a (pg. 10-18)
Q10-5 a (pg. 10-18)
Q10-6 d (pg. 10-17, Figure 10.22, pg. 10-18, Figure 10.23)
Q10-7 e (pg. 10-17)
Q10-8 c (pg. 10-19, 10-22)
Q10-9 c (pg. 10-19, 10-22)
Q10-10 e (pg. 10-19, 10-20)
Q10-11 c (pg. 10-19)
Q10-12 d (pg. 10-22)
Q10-13 a (pg. 10-21)
Q10-14 c (pg. 10-22)
Q10-15 b (pg. 10-23, Figure 10.32)
Q10-16 d (pg. 10-23)
Q10-17 d (pg. 10-14, 10-15)
Q10-18 b (pg. 10-24)
Q10-19 d (pg. 10-18, 10-25)
Q10-20 a (pg. 10-25)
Q10-21 e (pg. 10-14, Figure 10.16, pg. 10-15, Figure 10.18, pg. 10-20, 10-26, Figure 10.36)
Q10-22 b (pg. 10-24)
Q10-23 b (pg. 10-22)
Q10-24 a (pg. 10-17)
Q10-25 a (pg. 10-21)
Q10-26 c (pg. 10-2)
Q10-27 e (pg. 10-3)
Q10-28 e (pg. 10-4)
Q10-29 c (pg. 10-27, Figure 10.27)
Q10-30 b (pg. 10-27, Figure 10.27)
Q10-31 b (pg. 10-27, Figure 10.27)