Phase diagrams kp 4

Question 1

bestatigen Sie den Reduzierte Phasenregel// gibbs phase rule und finden Sie F [table 4.1]

Answer 1

[table 4.1]

Question 2

Lösen Sie die folgenden Fragen zur Hebelregel [table 4.2]

Answer 2

[table 4.2]

Question 3

[table 4.3]

Answer 3

[table 4.3]

Question 4

[table 4.4]

Answer 4

[table 4.4]

Question 5

[table 4.5]

Answer 5

[table 4.5]

Question 6

What are the α and α′ phases in a binary alloy system? [table 4.6]

Answer 6

α (alpha): The high‐temperature, disordered solid solution where A and B are randomly distributed.

α′ (alpha-prime): The ordered version (superstructure) that appears at lower temperatures when A and B occupy distinct sublattice sites.

Question 7

What is meant by “Überstruktur” (superstructure)? [4.7]

Answer 7

A superstructure forms when different atom types (A, B) systematically occupy particular sublattice sites, creating an ordered lattice variant of the same crystal structure.

Question 8

Was versteht man unter „intermetallischen“ oder „intermediären“ Verbindungen?

Answer 8

Intermetallische bzw. intermediäre Verbindungen sind chemische Verbindungen zwischen Metallen (oder Metall + Nichtmetall) mit metallischem Charakter. Sie weisen üblicherweise festgelegte Stöchiometrien auf und kristallisieren in einer eigenen Struktur, die sich von den Gittertypen der reinen Metalle unterscheidet.

Question 9

Was ist der Unterschied zwischen einer „intermediären Verbindung“ und einer „intermetallischen Verbindung“?

Answer 9

Intermediäre Verbindung: Allgemeiner Begriff für Verbindungen Metall–Metall oder Metall–Nichtmetall.

Intermetallische Verbindung: Bezieht sich konkret auf Metall–Metall-Verbindungen.