Lab 5: Amalgam Condensing/Carving Flashcards

1
Q

types of amalgam

A
  • dispersed phase (dispersalloy)

- spherical (tytin)

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
2
Q

setting speeds of amalgam

A
  • slow (6 min. working time)
  • regular (4-5 min)
  • fast (3 min)
How well did you know this?
1
Not at all
2
3
4
5
Perfectly
3
Q

size of amalgam

A
1 spill (0.8g)
2 spill (1.2g)
3 spill (1.6g)
How well did you know this?
1
Not at all
2
3
4
5
Perfectly
4
Q

gram weight of 1-spill

A

0.8g

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
5
Q

gram weight of 2-spill

A

1.2g

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
6
Q

gram weight of 3-spill

A

1.6g

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
7
Q

what do we use in operative preclinic?

A

dispersalloy (dispersed phase), regular set, 2-spill

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
8
Q

amalgam is a ________

A

high copper alloy

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
9
Q

occlusal surfaces shaped by _____ called the _______

A

egg burnisher, pre-carving burnish

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
10
Q

in carving, keep walls 3 carver ____ to cavosurface margin to prevent gouging

A

perpendicular

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
11
Q

irregular bits of material; what can they be removed by?

A

bits, walls 3/half hollenbeck,

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
12
Q

amalgam initially condensed in a ____ fashion, ______ to create a fish-scale look

A

step-wise, overlapping

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
13
Q

pre-carving burnisher in Class I

A

egg-burnisher

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
14
Q

pre-carving burnisher in Class V

A

PKT 3

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
15
Q

patients should not chew ____ for 24 hours (due to waiting for full strength of materials)

A

hard foods

How well did you know this?
1
Not at all
2
3
4
5
Perfectly
16
Q

1 hour after, material is at ___% of final strength

A

60%

17
Q

24 hours after, material is at ___% of final strength

A

90%

18
Q

new amalgam restorations may be sensitive to ___, due to ______

A

micro-leakage

19
Q

name for mixing amalgam in machine

A

trituration (mixing)

20
Q

working time for amalgam that we’re using

A

4.5 minutes

21
Q

time from trituration until amalgam looses plasticity and becomes crumbly

A

working time

22
Q

3 goals of condensation

A
  • adapting to walls/angles/margins
  • eliminating air voids/porosity
  • eliminating mercury-rich material