Closed book 4

Question 1

Profile RT may be used for measuring

Answer 1

nozzle thickness

Question 2

Minimum temperature for repair welding

Answer 2

0F or -20C

Question 3

PMI tools shall be calibrated

Answer 3

as specified by the manufacturer

Question 4

What material can be used to reduce the effect of CUI

Answer 4

Closed cell foam

Question 5

Arc blow is caused by

Answer 5

magnetic forces

Question 6

Inaccurate RT or UT results

Answer 6

do more UTT via A B or C scan (fucking dumb i know)

Question 7

Filler material is weaker than the parent, repair thickness must not be more than

Answer 7

50% of required thickness of base metal

Question 8

Stainless steel weld repairs in hydrogen service should be cooled down then tested by

Answer 8

PT (before UT after 24 hours)

Question 9

Safety aspects of hot tapping are found in

Answer 9

API 2201

Question 10

CDW is used for materials which are XXX than those that use PWHT

Answer 10

More brittle

Question 11

Examination point is

Answer 11

a recording point within a CML

Question 12

who is responsible for determining the amount of PMI required on materials for repair

Answer 12

Owner/user

Question 13

After CDW, the final weld layer should be

Answer 13

Ground flush to bare metal

Question 14

After repairs, for vessels susceptible to Brittle fracture

Answer 14

additional surface NDE requested by inspector

Question 15

Advantage of stud welding

Answer 15

can be used in any position

Question 16

Before removing a PRV what should be checked

Answer 16

connected piping

Question 17

what should be done if sulfidisation is anticipated

Answer 17

proactive & retroactive PMI programs

Question 18

Discontinuity usually found in the weld toe

Answer 18

overlap

Question 19

Clean fracture and low impact toughness shows that the material is

Answer 19

not tough

Question 20

Preferred method for finding SCC is

Answer 20

EC or PT

Question 21

if finding a gauge glass assembly vibrating, the inspector should

Answer 21

consult with a qualified engineer

Question 22

new vessels installed, with completed MDR, the inspector should

Answer 22

EXTERNAL inspection

Question 23

best method to mitigate caustic SCC in steam service

Answer 23

design

Question 24

insert plates can have the RT substituted by UT if

Answer 24

approved by the inspector

Question 25

CR is calculated by

Answer 25

thinnest or an average of readings

Question 26

Inspector must pass 510 &

Answer 26

may be a contractor acceptable to owner operator

Question 27

When does the nameplate need additional stamping or signing by the engineer

Answer 27

NEVER

Question 28

What MUST be in the vessel record

Answer 28

name plate

Question 29

Vessels in parallel process may be considered similar if

Answer 29

they have analogous and readily recognised similarities

Question 30

What inspections may be done on redundant vessels left in-situ

Answer 30

external visual inspection

Question 31

Carbon steel with carbon content above .3% may be used in repairs if

Answer 31

it is marked as per code requirement

Question 32

documentation oin file if service & location change

Answer 32

Process safety information

Question 33

Limitation of stud arc welding

Answer 33

plain carbon & low alloy steels only

Question 34

inspection organisation may belong to the owner and be authorised inspector if

Answer 34

its only inspecting its own equipment

Question 35

Direct current MT yoke must be able to lift XX

Answer 35

40 Lbs

Question 36

Bulging & buckling in a metallic lining indicated

Answer 36

a leak in lining or attachment welds

Question 37

Most important factor in determining a components resistance to fatigue cracking?

Answer 37

Design