Chloride Stress Corrosion Cracking (Cl-SCC Flashcards by Anibal Mavo | Brainscape

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Starts in ____ or____ surface

A

ID or OD

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

The cracks are:

A

Transgranular or intergranular

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Initiate in temperature >

A

140 °F

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

The mechanism live in presence of ______ enviroments, oxigen and Ph>

A

Chloride, 2

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Susceptible metal:

A

SS 300

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Critical range of % nickel

A

8-12%

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Duplex is less resistent?

A

no

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Good materials: CS, SS400, LAS and _____

A

Nickel based >35%

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Ph and temperature >___ and 140°F produce SCC

A

2

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Ph

A

2

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Exist in _______ equipments and systems:

A

condensedate

How well did you know this?

1

Not at all

2

3

4

5

Perfectly

Q

Chloride Stress Corrosion Cracking (Cl-SCC

Is visible the corrosión?

A

no

How well did you know this?

1

Not at all

2

3

4

5

Perfectly