Chloride Stress Corrosion Cracking Flashcards
1
Q
Chloride Stress Corrosion Cracking can cause cracks that normally initiate:
A
On the surface of 300 Series SS
2
Q
Which of the following is not a factor in the Chloride Stress Corrosion Cracking?
A
Pressure
3
Q
Which of the following can contribute to CI-SCC
A
Dissolved oxygen
4
Q
Heat transfer equipment can provide a way for chlorides to:
A
Concentrate
5
Q
CI-SCC usually occurs at a pH:
A
above 2
6
Q
CI-SCC usually occurs at temps above
A
140 F
7
Q
External CI-SCC has been caused by chlorides in:
A
paint